ABSTRACT
Soft linings are materials used to reduce the tension and forces of mastication, forming all or part of the fitting surface of a denture. This study evaluated the effect of thermocycling on waterabsorption, solubility, Shore A hardness and color stability of permanent soft liner materials. MATERIAL AND METHODS: Two chemically activated soft liner materials (Sofreliner S; GC Reline Ultrasoft) were tested. Twenty cylindrical specimens (30.0 x 1.0 mm) were prepared for measuring water absorption and solubility and another twenty (30.0 x 3 mm) for analyzing Shore A hardness and color stability. Color was measured by a spectrophotometer before and after 2000 thermocycles. A one-way ANOVA test and Tukey test at a 5% confidence level (p<0.05) were performed. RESULTS: The results did not show statistical differences for water absorption, solubility or color stability. The post-thermocycling Shore A hardness values were significantlyhigher than those before the treatment. CONCLUSION: Thermocycling of soft liner materials increased Shore A hardness.
Objetivo: Los materiales para rebasado tienen como propósito disminuir la tensión, la presión masticatoria en los tejidos de soporte y aumentar la retención de la dentadura, además de serindicados para prótesis buco-maxilo-faciales. El objetivo de este estudio fue evaluar el efecto del termociclado en los materiales para rebasado blandos considerados definitivos y evaluar lasalteraciones en relación a la absorción de agua, solubilidad, dureza Shore A y estabilidad de color. Materiales y Métodos: Dos materiales para rebasado blandos definitivos (Sofreliner S y GC Reline Ultrasoft) fueron examinados. Fueron confeccionados 20 muestras, midiendo 30 mm de diámetro x 1 mm deespesor, aquellos destinados al test de absorción y solubilidad y 20 muestras con 30 mm de diámetro x 3 mm de espesor para dureza y estabilidad de color. Fueron realizados los tests deabsorción y solubilidad. La dureza fue medida en un durometroy la estabilidad de color por medio de un spectrofotómetro en los periodos inicial y después de 2000 ciclos de termociclaje. Una vez obtenidos los datos, estos fueron submetidos al análisis de varianza (ANOVA) seguido por el test Tukey (p<0,05). Resultados:En relación a la absorción, solubilidad y estabilidad de color no hubo diferencia estadísticamente significativa entre losmateriales, en relación al test de dureza fue constatada una diferencia estadísticamente significativa entre los periodos y los materiales examinados. Conclusión: El termociclaje no interfirióen la absorción, solubilidad y estabilidad de color de los materiales evaluados, sin embargo interfirió de forma significativaen la dureza Shore A. Los materiales tuvieron sus valores promedios de dureza aumentados después del termociclaje.
Subject(s)
Denture Rebasing , Denture Rebasing/classification , Thermodynamics , Absorption , Analysis of Variance , Color , Hardness , Chemical Phenomena , SolubilityABSTRACT
Foi estudada histologicamente a reparação do alvéolo dental de ratos desidratados, após o implante de adesivo fibrínico (TISSUCOL®) associado à irrigação prévia da ferida com solução a 5% de ácido épsilon-aminocapróico. Foram empregados 72 ratos, divididos em três grupos, que receberam diferentes tratamentos após o procedimento cirúrgico. No Grupo I, após a extração do incisivo superior direito, a mucosa gengival foi suturada. Nos Grupos II e III foi provocada a desidratação crônica pela privação de ingestão de líquidos durante 09 dias (3 dias no pré-operatório e 6 dias no pós-operatório), sendo que, no Grupo II, após a extração dental, a mucosa gengival foi suturada de forma semelhante à do Grupo I; no Grupo III, logo após a exodontia, o alvéolo foi irrigado com a solução de ácido épsilon-aminocapróico a 5%, seguida de implante de adesivo fibrínico (TISSUCOL®) e foi feita sutura da mucosa de forma semelhante à dos demais grupos. Decorridos 3, 7, 15 e 21 dias após o ato operatório, os animais foram sacrificados em número de 6 para cada grupo. A seguir, as peças contendo o alvéolo dental foram removidas e fixadas em formalina a 10% e descalcificadas em solução de ácido fórmico e citrato de sódio em partes iguais. Após processamento laboratorial de rotina, foram incluídas em parafina para microtomia. Foram obtidos cortes semi-seriados com 6 micrômetros de espessura, seguidos de coloração em hematoxilina e eosina para estudo microscópico. Os resultados obtidos mostram que a hidroprivação no pré e pós-operatório ocasiona profundo retardo no processo de reparo em feridas de extração dental. O emprego de adesivo fibrínico (TISSUCOL®) melhora o quadro fibrinolítico provocado pela desidratação.